Leadsun Low cement castable is based on the use of low calcium aluminate cement content, and they are used in many applications that require high refractoriness, corrosion resistance and abrasion resistance. They possess a uniform structure with low porosity; have high temperature strength throughout the low and intermediate temperature range.
The content of CaO of low cement castable is usually less than 3%,so it insure the castable have a good strength in mid-temperature.
Item
LC75
LC80
LC85
LC95
Service Temp ℃
1650
1700
1750
1780
Bulk Density (g/cm3)
(Dried at 110℃)
2.55
2.6
2.7
3.0
CCS 110℃
(Mpa) 1100℃
1500 ℃
65
75
80
70
80
85
80
90
100
90
95
110
MOR 110℃
(Mpa) 1100℃
1500℃
9
10
11
10
11
12
11
12
13
13
14
15
Max Grain Size (mm)
6
6
6
6
Chemical Analysis(%)
Al2O3
CaO
Fe2O3
75
2-3
2.4
80
2-3
2.0
85
2-3
1.8
95
2-3
1.5
Application Guidelines
Mixer
Placement
Water/Mixer Temp℃
Mixing Time(Min):Dry/Wet
P
V/T
20±5
2/5
P
V/T
20±5
2/5
P
V/T
20±5
2/5
P
V/T
20±5
2/5
Water % (Typical)
7-9
7-9
6-8
6-7